Printable Non-Curable Thixotropic Hot Melt Composition

ABSTRACT

A printable non-curable thixotropic hot melt composition is described. The composition comprises non-curable holt melt waxes transformed into a thixotropic composition by the use of thickeners. The thickeners can be added separately to the hot melt wax or formed in-situ, either before or after application to the substrate. A process of forming such printable non-curable thixotropic hot melt composition is described.

RELATED APPLICATIONS

This application is a continuation-in-part of co-pending, commonlyassigned U.S. patent application Ser. No. 17/213,950, filed on Mar. 26,2021, the disclosure of which is incorporated herein by reference.

FIELD OF THE INVENTION

The present invention is directed to a non-curable thixotropic hot meltcomposition which can be used as a resist. In particular, the inventionis directed to such a non-curable hot melt thixotropic compositioncomprising waxes and thickeners. The resist can be used in an etching orplating process.

BACKGROUND OF THE INVENTION

The present invention is directed to hot melt compositions which can beused as plating resists and etch resists. Resists are used to producepatterns on substrates. Typically, a material is applied to thesubstrate. Various application methods have been developed to apply suchresist materials to substrates. For example, the resist can beselectively applied by methods, such as but not limited to controlleddepth dipping, ink jet printing, gravure printing, pad printing, andscreen printing. In each of these examples, the resist is applied to adesired area of the substrate and then fixed in place on the substrateby means including solvent evaporation, active heat to cross link theresist or by actinic radiation cure. Alternatively, the resist can beapplied to a substrate with the subsequent modification of the coveredareas. Examples of this include photoresist systems which rely onselective exposure of the initial resist with actinic radiation througha mask followed by a development step or non-photosensitive systems inwhich selective removal can be done using ablation or manually usingscraping tools. The substrate is then plated with a metal in a platingbath or exposed to an etching process. The resist can then be removedafter the plating or etching process in a stripping bath. The resistmust be able to withstand the plating or etching process bath but alsobe readily removed in the stripping bath.

U.S. Pat. No. 3,644,180 describes the chemical treatment of surfaces toselected portions of the surface by applying inorganic resists to thesurface in a desired pattern. Silicon dioxide is deposited at a lowtemperature on a titanium surface surrounding a platinum interconnectionpattern on a silicon semiconductor.

U.S. Pat. No. 4,877,644 describes a method for the selective plating ofa metal substrate on which a thin polymeric plating resist is applied,followed by the selective removal of the resist to expose portions ofthe substrate to plating. Laser ablation is used to selectively removethe resist prior to plating.

U.S. Pat. No. 6,713,529 B2 describes a hot melt ink for use with an inkjet printing apparatus which is a liquid at about 100° C. to about 130°C. The ink solidifies to a two-phase solid having an elastic phase and acrystalline phase. The ink is formulated from a carrier, a firstplasticizer, a flow additive and a colorant.

EP 1090079 B1 discloses a radiation curable composition suitable for usein hot melt inkjet printers. The composition comprises 35-98% by weightof a radiation curable material and a thickener. The composition is athixotropic paste at 20° C. The composition also has a viscosity of lessthan 25 centipoise at a temperature in the range of from 40° C. to 130°C.

A process for etching or plating is described in U.S. Pat. No. 8,999,185B2. The process comprises the steps of ink jet printing an alkaliremovable water insoluble hot melt ink jet onto a substrate to form aresist image. The substrate is etched or plated in an aqueous medium.The resist image is then removed with an aqueous alkali.

U.S. Pat. No. 8,252,506 B2 describes hot melt compositions which includeacid waxes and acrylate functional monomers free of acid groups. Uponapplication of actinic radiation, the hot melt compositions cure to forma resist. The resist can be used as an etch resist or a plating resist.The resist is then stripped from the substrate. The hot meltcompositions can be used in the manufacture of printed circuit boards,optoelectronic and photovoltaic devices.

UV curable hot melt resists have been developed for use in inkjetprinting processes. Hot melt resists are solids at ambient temperaturesand turn to liquids during inkjet printing processing at hightemperature, which are above the melting temperatures of the hot meltresists. As inkjet printers eject the droplets of liquid hot melt resistto the surface of plating parts, the droplets form pre-designed patternsas the droplets cool down on the surface. The UV light is then appliedto cure these hot melt resists to form the protective masks. Many of thehot melt resist formulations comprise UV curable monomers and waxes withacid functional groups. The use of the hot melt resists is advantageousover other types of resists because the inkjet printer can easily printpre-designed patterns digitally with high resolutions, can easily beapplied on parts with complex shapes, and can eliminate the need for thelaser ablation process. However, such hot melt resists still involve aUV curing process and the need for special UV equipment to be used inthe process.

Non-curable hot melt resists have been used as plating masks. Many hotmelt resist waxes are compatible with high efficiency plating processesbut do not work as well with low efficiency plating process such as goldplating. Low efficiency gold plating can generate gases which can causedamage to the edges of resist features masks, resulting in platingfailures. Broken edges during plating can also be due to the highflowability of the hot melt resist on plating surfaces, which leads tothin edge formation during printing.

The non-curable hot melt waxes need to have low viscosities underprinting temperatures, which requires them to have low molecularweights. The mechanical strength of these low molecular weight waxesresults in the waxes being very brittle. The brittleness of the waxesand thin edges of the wax masks result in the edges of the mask havingvery limited resistance to the forces from gas evolution during theplating process. To solve this problem of brittleness, severalapproaches have been proposed, such as improving the strength ortoughness of the wax as well as pre-cooling the plating parts to limitwax flowability after the parts are printed. However, improving thestrength or toughness of the waxes may lead to printing viscosityincreases as well as increasing the difficulty of stripping the waxesafter the plating process. Pre-cooling the plating parts requiresadditional equipment and changes in the process.

It would, therefore, be beneficial to provide a non-curable hot meltthixotropic composition which eliminates the problems described above.In particular, it would be beneficial to provide non-curable thixotropichot melt compositions which can be used as resists.

SUMMARY OF THE INVENTION

An embodiment is directed to a printable non-curable thixotropic hotmelt wax used for resists. The printable non-curable thixotropic hotmelt wax includes one or more waxes with an acid functional group, ananhydride group or an amine functional group. The printable non-curablethixotropic hot melt wax also includes a thickener comprising fumedsilica, polymeric particles, or metallic complexes.

An embodiment is directed to a printable non-curable thixotropic hotmelt wax used for resists having a mixture of waxes and a thickener. Themixture of waxes includes waxes having an acid functional group, ananhydride group, or an amine functional group. The thickener is miscibleor partially miscible with the mixture of waxes at a temperaturesufficiently high to melt the thickener.

An embodiment is also directed to a process to form fine and uniformthickener particles in a mixture of a wax and a thickener componentresulting in a non-curable thixotropic hot melt composition. The processincludes heating the mixture of wax and thickener component to achievecomplete mixing of the wax and thickener component; and cooling down themixture under high speed rotation, stirring, shaking, vibration orshear, resulting in the precipitation of the thickener materials to formfine particles in the composition.

Yet another embodiment is provided in which the printable non-curablethixotropic wax is used as either an etching resist or plating resist inwhich the thickener precipitates after the mixture is applied to thesubstrate.

Other features and advantages of the present invention will be apparentfrom the following more detailed description of the illustrativeembodiment, which illustrates, by way of example, the principles of theinvention.

DETAILED DESCRIPTION OF THE INVENTION

In the description of embodiments of the invention disclosed herein, anyreference to direction or orientation is merely intended for convenienceof description and is not intended in any way to limit the scope of thepresent invention. Relative terms such as “lower,” “upper,”“horizontal,” “vertical,” “above,” “below,” “up,” “down,” “top” and“bottom” as well as derivative thereof (e.g., “horizontally,”“downwardly,” “upwardly,” etc.) should be construed to refer to theorientation as then described or as shown in the drawing underdiscussion. These relative terms are for convenience of description onlyand do not require that the apparatus be constructed or operated in aparticular orientation unless explicitly indicated as such. Terms suchas “attached,” “affixed,” “connected,” “coupled,” “interconnected,” andsimilar refer to a relationship wherein structures are secured orattached to one another either directly or indirectly throughintervening structures, as well as both movable or rigid attachments orrelationships, unless expressly described otherwise.

Moreover, the features and benefits of the invention are illustrated byreference to the preferred embodiments. Accordingly, the inventionexpressly should not be limited to such embodiments illustrating somepossible non-limiting combination of features that may exist alone or inother combinations of features, the scope of the invention being definedby the claims appended hereto.

The invention is directed to a non-curable, thixotropic hot meltcomposition formed by combining a hot melt wax with a thickener. The waxis converted into a thixotropic composition which can be used as aresist. The non-curable, thixotropic hot melt composition is preferablyprintable. In this specification, the term “non-curable” includes anycomposition that cannot be cured under conventional conditions,including but not limited to exposure to UV light, heat or moisture.

Illustrative embodiments of the invention are directed to convertingnon-Newtonian hot melt waxes into printable non-curable thixotropic hotmelt waxes which are used as resists by adding the thickeners to suchwaxes. By converting these non-curable waxes into non-curablethixotropic hot melt waxes, they can still be printable under high shearrate and printing temperatures. However, the droplets of these printablenon-curable thixotropic hot melt waxes will not flow and will not formthin edges after application to the parts due to their high viscosityunder low shear rate.

Examples of suitable non-Newtonian non-curable hot melt waxes which canbe used in the instant invention, include, but are not limited to,LS2535 wax or LS2538 wax, both manufactured by Koster Keunen, Inc.Preferably, these waxes are blends of polyolefin waxes having one ormore types of acid functional group. Many other non-curable hot meltwaxes which are printable can also be used in the hot melt non-curablethixotropic composition of the instant invention. For example, foracidic gold and palladium plating waxes, the waxes must have an acidfunctional group or anhydride functional group so they can withstand theacidic plating solution but can be stripped off in a basic (or alkaline)solution after plating. Examples of suitable non-curable hot melt waxesto be used as gold and palladium plating waxes include but are notlimited to Licowax S flakes acid wax from Clariant AG and stearic acid.For alkaline plating solutions such as cyanide silver plating waxes, thewaxes must have an amine functional group so they can withstand thealkaline plating solution and be stripped off in acid solution afterplating. Examples of suitable non-curable hot melt waxes that can beused in silver plating include but are not limited to octadecylamine andFentamine DA102 from Solvay S.A. Mixtures of the various waxes can beused provided the desired properties of the thixotropic hot meltcomposition are obtained.

Thickeners such as fumed silica, polymeric particles, or metal complexescan be added to the wax to form the printable non-curable thixotropichot melt composition of this invention. For a composition which is usedin inkjet printing, the preferred size of the thickener particles isless than one tenth of the nozzle size of the inkjet printer. Inillustrative embodiments, the size of the thickener particles is tenmicrons or less. Any thickener that exhibits thickening efficiency andhas the small size required may be used. The amount by weight of fillerscan be between approximately 0.50% to approximately 30% by weight of thetotal composition.

In one example, a non-Newtonian non-curable hot melt wax (LS2535) wasconverted into a non-curable thixotropic hot melt wax by adding fumedsilica to the wax. Examples of suitable fumed silicas include but arenot limited to, Aerosil 200 and Aerosil R974, both manufactured byEvonik Industries. The sizes of fumed silica particles are generallysub-micron. Such thickeners can be between approximately 0.50% toapproximately 5% by weight of the total composition. The resultantnon-curable thixotropic wax exhibited strong shear thinning character.The resultant non-curable thixotropic hot melt waxes have highviscosities under low shear rate and slightly higher viscosities underhigh shear rate when compared with a control sample which is theformulation without the thickener. The viscosities of the resultantnon-curable thixotropic hot melt wax can be further lowered under highershear rate present in the printer. The viscosity of the resultantnon-curable thixotropic hot melt wax can also be adjusted by theaddition of low viscosity acid waxes such as stearic acid. The amount ofthe low viscosity acid wax to be added is well within the scope of oneof ordinary skill in the art.

Fumed silica can form aggregations if processed in an inkjet printerduring the dispersion process due to its high surface area and surfaceproperty compatibility to the plating wax. Additionally, the fumedsilica can precipitate from the composition. Therefore, it is desirableto use a fumed silica which is highly compatible with the wax used.

Polymeric particles or micron size powder products may also be used asthickeners in the composition of the instant invention. One or moretypes of polymeric particles may be used. Preferably the polymericparticles are polyolefin particles. An example of polyolefin particlesare polyethylene particles. The polymeric particles must have highenough melting points to be above the mixing and printing temperature ofthe composition so as to survive the mixing and printing process.Generally, small particle sizes for the polymeric particles or powderproducts give better thickening and thixotropic performance. Forpolymeric particles, precipitation and low shear thinning efficiency mayneed to be considered. An example of a polymeric particle is MPP-635XFhigh molecular weight polyethylene wax from Micro Powders Inc.Preferably, the mean particle size is from about 4 to about 6 microns.In one embodiment, the polymeric micron powder product used as athickener is between approximately 5% to approximately 20% by weight ofthe composition.

In addition to the above thickeners, metallic complexes can also be usedto transform the waxes to the printable non-curable hot meltcompositions of the instant invention. Examples of such include but arenot limited to lithium complexes and aluminum complexes.

Other thickeners can be incorporated into the non-curable thixotropichot melt composition of the instant invention. Examples of such otherthickeners include, but are not limited to, aerogel, carbon nanotubes,graphene and other inorganic or organic micron or nano particles. Thesethickeners may also be used so long as the hot melt composition retainsits desired properties and they can be dispersed in the wax to form athixotropic composition.

Other additives may be included in the composition in conventionalamounts provided that the additives do not detract from the thixotropicproperties of the composition. Examples of such additives include dyes,opacifiers, antistatic agents, foaming agents, plasticizers, binders,antioxidants, surfactants, antistatic agents, metal adhesion agents andstabilizers. Such additives may be included in conventional amounts.

Another embodiment of the instant invention uses the in-situ formationof thickeners in a hot melt wax, to form the non-curable thixotropic hotmelt composition. In this specific embodiment, a thickener component isused to form the thickener and therefore provide the thixotropicproperties to the wax. In this particular embodiment, the thickenercomponent must have a different solubility than the rest of thecomposition under different temperatures using the process of theinstant invention. The thickener component must be miscible or partiallymiscible with the other components of the composition. The thickenercomponent, the wax and other components of the composition are mixed ata temperature to achieve complete mixing. The temperature can be easilychosen by one of ordinary skill in the art in this embodiment dealingwith the in-situ formation of thickeners. When the composition is cooledto a lower temperature with vigorous stirring or other agitation, thethickener component precipitates to form fine particles and therebyrenders the composition thixotropic.

The amount by weight of thickener component of the total composition isbetween approximately 0.5% to approximately 20% by weight, preferablybetween approximately 1% to approximately 5% by weight. Examples ofthickener components that can be used in the instant invention includebut are not limited to Licocene PP 6102 granules from Clariant A.G. (lowviscous metallocene catalyzed polypropylene wax), Licocene PP MA 6252granules from Clariant A.G. (maleic anhydride grafted polypropylenewax), A-C 540 ethylene acrylic acid copolymer from HoneywellInternational, Inc. and A-C 325 high density oxidized polyethylenehomopolymer from Honeywell International, Inc.

To obtain the in-situ formation of the thickener, the thickenercomponent and the hot melt wax are heated to a temperature that issufficiently high so as to achieve mixing of the thickener component andthe hot melt wax. In an embodiment, the mixing temperature isapproximately 10° C. to approximately 30° C. above the meltingtemperature of thickener component. The heating time depends upon howlong it takes the thickener component and plating wax to be completelymixed.

With the thickener component fully mixed with the hot melt wax, thecomposition is cooled down. As the mixture is cooled down, it issubjected to high speed rotation, stirring, shaking or vibration, forexample, by the use of a speed mixer or other equipment. In anillustrative embodiment, the mixture is cooled down to a temperaturewhich is approximately 10° C. to approximately 30° C. below the meltingtemperature of the wax.

Under these conditions, the thickener component will precipitate fromthe wax to form fine particles due to its reduced solubility. As aresult, small solid particles down to micron size are formed due tovigorous shear or shaking before the composition solidifies. The solidparticles function as thickeners for the wax forming the non-curablethixotropic hot melt composition of the instant invention.

In another embodiment of the invention, thickener particles areuniformly dispersed in a mixture of hot melt waxes. Preferably in thisembodiment, the thickener particles are organic. The thickener, the hotmelt wax and any other additives are mixed at a temperature to achievecomplete mixing. Generally, the temperature of mixing is determined bythe component in the mixture with highest melting point. Preferably, thecomposition is mixed at about 10 to about 50° C. above the meltingtemperature of the thickener. After being mixed, the composition is thendeposited on the substrate. Preferably the composition is deposited onthe substrate by an inkjet printer. After the composition is deposited,the thickener starts to precipitate and form small particles andconverts the mixture into a thixotropic composition with reducedflowability, preventing formation of thin resist edges.

In this embodiment, the amount by weight of the thickener component ofthe total composition is between approximately 0.1% to about 20% byweight, preferably between approximately 1% to approximately 10% byweight. Examples of suitable thickeners to be used in this embodimentinclude polyethylene waxes. Preferably, the polyethylene waxes are lowermolecular weight polyethylenes and have a molecular weight in the rangeof about 400 to about 1000. In addition, the melting point of thepolyethylene wax used in this embodiment is between 70° C. to 110° C.,preferably between 80° C. and 100° C. An example of a suitablepolyethylene wax to be used in the instant invention is Polywax® wax,available from Baker Hughes, Inc.

Once the mixed composition is applied to the substrate, the thickenerstarts to precipitate as the composition cools and forms small particlesdue to its high crystallization temperature and limited solubility inthe hot melt wax. These precipitated thickener particles convert themixture containing the hot melt wax into a thixotropic hot meltcomposition with reduced flowability. This embodiment provides forimproved printability of the printable non-curable thixotropic hot meltcomposition.

In yet another embodiment of the invention, a component is added to thewax to form a non-curable hot melt composition of the instant invention.The component is not miscible with the wax. This component is thendispersed to form fine particles under a sufficiently vigorous mixingprocess.

The printable non-curable thixotropic hot melt composition of theinstant invention can be used as a resist. The resist can be used as anetch resist or a plating resist. In general, the resist is selectivelydeposited on a substrate. Hot melt compositions are typically applied byinkjet printers. In addition, the hot melt resist compositions of theinstant invention can be applied using screen printing or by sprayapparatus having nano- to macro-deposition capability. All of these areknown methods in the art and can be used to apply the printablenon-curable thixotropic hot melt composition of the instant invention toa substrate.

If used as an etch resist, the uncovered section of the substrate may beetched to a desired depth. The etchant does not remove the resist fromthe substrate during etching, therefore, the composition functions as anetch resist. The etch resist is then stripped from the substrate leavinga patterned substrate which can be further processed using conventionalmethods known in the art. In the alternative, the substrate may beplated with a metal to form a pattern on the substrate, thus the resistfunctions as a plating resist. The plating resist is then stripped fromthe substrate leaving a substrate with a metal pattern for furtherprocessing by conventional methods known in the art.

Etching can be done by methods known in the art appropriate to thematerial of which the substrate is composed. Typically, etching is donewith acids, such as hydrofluoric acid, nitric acid, phosphoric acid,hydrochloric acid, organic acids such as carboxylic acids and mixturesthereof, or with industrial etches such as cupric chloride and ferricchloride. Such etches are well known in the art and may be obtained fromthe literature.

Etching is typically done at temperatures of 20° C. to 100° C., moretypically from 25° C. to 60° C. Etching includes spraying or dipping theresist coated substrate with the etchant in either a vertical orhorizontal position. Typically, spraying is done when the substrate isin the horizontal position. This allows for quicker removal of theetchant. The speed of etching may be accelerated by agitating theetchant, for example using sonic agitation or oscillating sprays. Afterthe substrate has been treated with the etchant it is typically rinsedwith water to remove traces of the etchant.

One or more metal layers may be deposited in the pattern formed on thesubstrate. Metals may be deposited electroless, electrolytically, byimmersion or light induced plating. Conventional electroless,electrolytic and immersion baths and methods may be used to depositmetal or metal alloy layers. Many such baths are commercially availableor described in the literature. Metals include but are not limited tonoble and non-noble methods and their alloys. Examples of such suitablenoble metals are gold, silver, platinum, palladium and their alloys.Examples of suitable non-noble metals are copper, nickel, cobalt,bismuth, zinc, indium, tin, and their alloys.

The hot melt composition wax can be used on various substrates,including but not limited to semiconductors, photovoltaic or solarcells, components for electronic devices such as lead frames and printedcircuit boards, in metal finishing of parts and precision tooling.

After being deposited on the desired substrate as part of the platingprocess, the non-curable hot melt composition can be removed from thesubstrate using a stripping bath. For a resist that is stable in an acidplating bath, the resist would be strippable in an alkali strippingbath. For a resist that is stable in an alkaline plating bath, theresist would be strippable in an acidic stripping bath.

While the invention has been described with reference to a preferredembodiment, it will be understood by those skilled in the art thatvarious changes may be made and equivalents may be substituted forelements thereof without departing from the spirit and scope of theinvention as defined in the accompanying claims. One skilled in the artwill appreciate that the invention may be used with many modificationsof structure, arrangement, proportions, sizes, materials and componentsand otherwise used in the practice of the invention, which areparticularly adapted to specific environments and operative requirementswithout departing from the principles of the present invention. Thepresently disclosed embodiments are therefore to be considered in allrespects as illustrative and not restrictive, the scope of the inventionbeing defined by the appended claims, and not limited to the foregoingdescription or embodiments.

1. A printable non-curable thixotropic hot melt composition for use as aresist during a plating process comprising: one or more hot melt waxeswith an acid functional group, an anhydride group, or an aminefunctional group; and a thickener comprising fumed silica, polymericparticles, or metallic complexes.
 2. The printable non-curablethixotropic hot melt composition as set forth in claim 1, wherein theprintable non-curable thixotropic hot melt composition can be strippedoff in a bath during a plating process.
 3. The printable non-curablethixotropic hot melt composition as set forth in claim 1, wherein theprintable non-curable thixotropic hot melt composition has a meltingtemperature above 50° C. and below 90° C.° C.
 4. The printablenon-curable thixotropic hot melt composition as set forth in claim 1,wherein the printable non-curable thixotropic hot melt composition isstable during said plating process.
 5. The printable non-curablethixotropic hot melt composition as set forth in claim 1, wherein saidthickener has a particle size that is less than ten microns.
 6. Theprintable non-curable thixotropic hot melt composition as set forth inclaim 1, wherein the amount of thickener is between approximately 0.50%to approximately 30% by weight of said composition.
 7. A printablenon-curable thixotropic hot melt composition used for plating resistsusing an inkjet printer comprising: a mixture of waxes with acidfunctional groups, anhydride groups or amine functional groups; athickener component that is miscible or partially miscible with themixture of waxes.
 8. The printable non-curable thixotropic hot meltcomposition as recited in claim 7, wherein the inkjet printablenon-curable thixotropic hot melt composition can be stripped off insolution stripping bath during the plating process.
 9. The printablenon-curable thixotropic hot melt composition recited in claim 7, whereinsaid hot melt composition has melting temperature above approximately50° C. and below approximately 90° C.
 10. The printable non-curablethixotropic hot melt composition as recited in claim 7, wherein saidcomposition is stable during a plating process.
 11. A process to formfine and uniformly dispersed thickener particles in a mixture of waxescomprising: heating the mixture of waxes and a thickener component to atemperature to achieve complete mixing; and cooling down the mixture ofwaxes and thickener component under high speed rotation, stirring,shaking, vibration or shear, wherein said thickener componentprecipitates from the mixture forming uniformly dispersed thickenerparticles.
 12. The process as recited in claim 11, wherein the mixtureof waxes and said thickener component is heated to a temperature betweenapproximately 10° C. to approximately 30° C. above the meltingtemperature of the thickener component.
 13. The process as recited inclaim 11, wherein the thickener component is miscible or partiallymiscible with the waxes at a temperature sufficiently high to melt thethickener component.
 14. A printable non-curable thixotropic hot meltcomposition for use as a resist during a plating process whichcomprises: one or more hot melt waxes with an acid functional group, ananhydride group, or an amine functional group; and a thickenercomprising polymeric particles.
 15. The printable non-curablethixotropic hot melt composition of claim 14, wherein the amount ofthickener is between approximately 0.1% by weight to approximately 20%by weight of the composition.
 16. A process to form fine and uniformlydispersed thickener particles in a mixture of hot melt waxes resultingin a thixotropic composition comprising: heating the mixture of waxesand a thickener component to achieve complete mixing; dispensing themixture of hot melt waxes and thickener component onto a desiredsubstrate, whereby the mixture is cooled and the thickener componentprecipitates to form a non-curable thixotropic hot melt composition. 17.A resist composition comprising a non-curable hot melt compositioncomprising one or more hot melt waxes with acid functional groups,anhydride groups or amine functional groups; and a thickener comprisingpolymeric particles.
 18. The resist composition of claim 17, whereinsaid thickener comprises polyethylene wax.
 19. The printable non-curablethixotropic hot melt composition of claim 14, wherein said polymericparticles comprise polyethylene wax.
 20. A printable non-curablethixotropic hot melt composition used as an a etch resist comprising:one or more hot melt waxes with an acid functional group, an anhydridegroup, or an amine functional group; a thickener comprising fumedsilica, polymeric particles, or metallic complexes.